Characterization of Conventional and High-Translucency Y-TZP Dental Ceramics Submitted to Air Abrasion

Abstract This study evaluated the effect of air-abrasion on t®m phase transformation, roughness, topography and the elemental composition of three Y-TZP (Yttria-stabilized tetragonal zirconia polycrystal) dental ceramics: two conventional (Lava Frame and IPS ZirCad) and one with high-translucency (Lava Plus). Plates obtained from sintered blocks of each ceramic were divided into four groups: AS (as-sintered); 30 (air-abrasion with 30 mm Si-coated Al2O3 particles); 50 (air-abrasion with 50 mm Al2O3 particles) and 150 (air-abrasion with 150 mm Al2O3 particles). After the treatments, the plates were submitted to X-ray diffractometry; 3-D profilometry and SEM/EDS. The AS surfaces were composed of Zr and t phases. All treatments produced t®m phase transformation in the ceramics. The diameter of air-abrasion particles influenced the roughness (150>50>30>AS) and the topography. SEM analysis showed that the three treatments produced groove-shaped microretentions on the ceramic surfaces, which increased with the diameter of air-abrasion particles. EDS showed a decrease in Zr content along with the emergence of O and Al elements after air-abrasion. Presence of Si was also detected on the plates air-abraded with 30 mm Si-coated Al2O3 particles. It was concluded that irrespective of the type and diameter of the particles, air-abrasion produced t®m phase transformation, increased the roughness and changed the elemental composition of the three Y-TZP dental ceramics. Lava Plus also behaved similarly to the conventional Y-TZP ceramics, indicating that this high translucency ceramic could be more suitable to build monolithic ceramic restorations in the aesthetic restorative dentistry field.

Resumo Este estudo avaliou o efeito da abrasão a ar na transformação de fase t®m, na rugosidade, topografia e composição elementar de três cerâmicas Y-TZP (Zircônia tetragonal policristalina estabilizada por ítrio): duas convencionais (Lava Frame e ZirCad) e uma de alta translucidez (Lava Plus). Placas obtidas de blocos sinterizados de cada cerâmica foram divididos em quatro grupos: AS (pré-sinterizado); 30 (jateamento com partículas de Al2O3 de 30 mm cobertas com Si); 50 (jateamento com partículas de Al2O3 de 50 mm) e 150 (jateamento com partículas de Al2O3 de 150 mm). Após os tratamentos, as placas foram submetidas à difratometria de Rx, perfilometria 3-D e microscopia eletrônica de varredura com espectroscopia de energia dispersiva de Rx (SEM/EDS). As superfícies pré-sinterizadas apresentaram predominantemente Zr e fase tetragonal. Todos os tratamentos superficiais produziram transformação t®m nas cerâmicas avaliadas. A topografia e a rugosidade foram influenciadas pelo diâmetro das partículas abrasivas (150>50>30>AS). A análise através de SEM mostrou que os três tratamentos produziram fendas retentivas nas superfícies das cerâmicas, por influência do tamanho das partículas. A análise através de EDS mostrou uma diminuição da concentração de Zr, paralela ao surgimento de O e Al, após o jateamento. No grupo tratado com partículas de Al2O3 de 30 mm cobertas com Si foi também observado um aumento de Si após o jateamento. Concluiu-se que, independente do tipo e do diâmetro das partículas, o jateamento produziu transformação t®m, aumentou a rugosidade e alterou a composição elementar das cerâmicas avaliadas. A Lava Plus apresentou comportamento semelhante às cerâmicas convencionais, indicando que esta cerâmica de alta translucidez pode ser mais adequada à confecção de restaurações monolíticas no campo da odontologia estética restauradora.

Avaliação de hipersensibilidade dentinária em função do procedimento clareador: revisão de literatura / Literature review: evaluation of dentin hypersensitivity after tooth bleaching procedures

O clareamento dental como tratamento estético em Odontologia tem sido amplamente empregado nos últimos anos e, visando o melhoramento deste, técnicas e produtos passaram por modificações. Todavia, ainda são encontrados alguns problemas que devem ser contornados. A sensibilidade pós-clareamento afeta mais da metade dos pacientes em diferentes graus. O presente estudo objetiva revisar os principais métodos empregados atualmente para reduzir essa incidência e/ou intensidade, podendo ser utilizados alguns protocolos nas fases pré, trans e pós-operatórias. Entre eles, destacam-se a escolha da técnica e da concentração do gel, uso de dessensibilizantes, aplicação tópica de flúor e administração de analgésicos e anti-inflamatórios.

Tooth bleaching procedures have been largely used. Techniques and products were improved along the years. However, some problems are still present and must be surpassed. Dentin hypersensitivity after tooth bleaching affects over fifty percent of pacients, in different levels. The present study aimed to review the current literature on the methods available to prevent and reduce the incidence and the intensity of hypersensitivity, using clinical protocols before, during and after the bleaching procedure. Among them, we highlight the choice of the technique and gel concentration, use of desensitizing agents and fluoride application, and administration of analgesics and anti-inflammatory.

Long-term degradation of resin-based cements in substances present in the oral environment: influence of activation mode

Indirect restorations in contact with free gingival margins or principally within the gingival sulcus, where the presence of organic acids produced by oral biofilm is higher, may present faster degradation of the resin-based cement pellicle. Objectives To investigate the degradation of four resin-based cements: Rely X ARC (R), Variolink II (V), Enforce (E) and All Cem (A), after immersion in distilled water (DW), lactic acid (LA) and artificial saliva (AS) and to analyze the influence of the activation mode on this response. Material and Methods Two activation modes were evaluated: chemical (Ch) and dual (D). In the dual activation, a two-millimeter thick ceramic disk (IPS Empress System) was interposed between the specimen and light-curing unit tip. Specimens were desiccated, immersed in distilled water, artificial saliva and lactic acid 0.1 M at 37°C for 180 days, weighed daily for the first 7 days, and after 14, 21, 28, 90 and 180 days and were desiccated again. Sorption and solubility (µg/mm 3 ) were calculated based on ISO 4049. The data were submitted to multifactor analysis of variance (MANOVA) and Tukey's HSD test for media comparisons (α=0.05). Results Sorption was higher after immersion in LA (p<0.05) and increased significantly with time (p<0.05). Sorption was influenced by the activation mode: Ch>D (p<0.05). The lowest solubility was presented by R (p<0.05). Conclusions Lactic acid increased the degradation of resin-based cements. Moreover, the physical component of activation, i.e., light-activation, contributed to a low degradation of resin-based cements. .

A critical analysis of the degree of conversion of resin-based luting cements

OBJECTIVE: This study analyzed the degree of conversion (DC percent) of four resin-based cements (All Ceram, Enforce, Rely X ARC and Variolink II) activated by two modes (chemical and dual), and evaluated the decrease of DC percent in the dual mode promoted by the interposition of a 2.0-mm-thick IPS Empress 2 disc. MATERIAL AND METHODS: In the chemical activation, the resin-based cements were prepared by mixing equal amounts of base and catalyst pastes. In the dual activation, after mixing, the cements were light-activated at 650 mW/cm² for 40 s. In a third group, the cements were light-activated through a 2.0-mm-thick IPS Empress 2 disc. The DC percent was evaluated in a FT-IR spectrometer equipped with an attenuated total reflectance crystal (ATR). The data were analyzed by two-way ANOVA and Tukey's HSD test. RESULTS: For all resin-based cements, the DC percent was significantly higher with dual activation, followed by dual activation through IPS Empress 2, and chemical activation (p<0.05). Irrespective of the activation mode, Rely X presented the highest DC percent (p<0.05). Chemically activated Variolink and All Ceram showed the worst results (p<0.05). The DC percent decreased significantly when activation was performed through a 2.0-mm-thick IPS Empress 2 disc (p<0.05). CONCLUSION: The results of the present study suggest that resin-based cements could present low DC percent when the materials are dually activated through 2.0 mm of reinforced ceramic materials with translucency equal to or less than that of IPS-Empress 2.